| According to DIN 1630 Test at elevated temperature test Temperature 250°C wall Thickness: 40 - 65 mm ; yield strength: 180 MPa |
| According to DIN 1630 wall Thickness: < 16 mm ; yield strength: 420 - 550 MPa |
| According to DIN 1630 wall Thickness: 16 - 40 mm ; yield strength: > 265 MPa |
| According to DIN 1630 wall Thickness: 16 - 40 mm ; yield strength: 420 - 550 MPa |
| According to DIN 1630 wall Thickness: 40 - 65 mm ; yield strength: > 255 MPa |
| According to DIN 1630 wall Thickness: 40 - 65 mm ; tensile strength: 420 - 550 MPa |
| According to DIN 1630 Condition NBK note annealing in a protective atmosphere or vacuum. |
| According to DIN 1630 Condition NBK wall Thickness: < 16 mm ; yield strength: > 265 MPa |
| According to DIN 1630 Condition NBK wall Thickness: < 16 mm ; yield strength: 410 - 550 MPa |
| According to DIN 1630 Condition NBK wall Thickness: 16 - 40 mm ; yield strength: > 255 MPa |
| According to DIN 1630 Condition NBK wall Thickness: 16 - 40 mm ; yield strength: 410 - 550 MPa |
| According to DIN 1630 Condition NBK wall Thickness: 40 - 65 mm ; yield strength: > 245 MPa |
| According to DIN 1630 Condition NBK wall Thickness: 40 - 65 mm ; tensile strength: 410 - 550 MPa |
| According to DIN 1630 Longitudinal specimens elongation: > 21 % |
| According to DIN 1630 Longitudinal samples Job blow KV at 20°C [68°F]: > 43 j |
| According to DIN 1630 Transverse specimens elongation: > 19 % |
| According to DIN 1630 Transverse samples Job blow KV at 20°C [68°F]: > 27 j |
| According to DIN 1630 Test at elevated temperature test Temperature 50°C wall Thickness: < 16 mm ; yield strength: 275 MPa |
| According to DIN 1630 Test at elevated temperature test Temperature 50°C wall Thickness: 16 - 40 mm ; yield Limit: 265 MPa |
| According to DIN 1630 Test at elevated temperature test Temperature 50°C wall Thickness: 40 - 65 mm ; yield strength: 255 MPa |
| According to DIN 1630 Test at elevated temperature test Temperature 200°C wall Thickness: < 16 mm ; yield strength: 215 MPa |
| According to DIN 1630 Test at elevated temperature test Temperature 200°C wall Thickness: 16 - 40 mm ; yield strength: 205 MPa |
| According to DIN 1630 Test at elevated temperature test Temperature 200°C wall Thickness: 40 - 65 mm ; yield strength: 200 MPa |
| According to DIN 1630 Test at elevated temperature test Temperature 200°C test Temperature 250°C wall Thickness: < 16 mm ; yield strength: 195 MPa |
| According to DIN 1630 Test at elevated temperature test Temperature 250°C wall Thickness: 16 - 40 mm ; yield strength: 185 MPa |
| According to DIN 1630 Test at elevated temperature test Temperature 250°C wall Thickness: 40 - 65 mm ; yield strength: 180 MPa |
| According to DIN 1630 Test at elevated temperature test Temperature 300°C wall Thickness: < 16 mm ; yield strength: 165 MPa |
| According to DIN 1630 Test at elevated temperature test Temperature 300°C wall Thickness: 16 - 40 mm ; yield strength: 160 MPa |
| According to DIN 1630 Test at elevated temperature test Temperature 300°C wall Thickness: 40 - 65 mm ; yield strength: 155 MPa |
| Density: 7.85 g / cm3 |