1.0238
Классификация
| Страна |
Раздел |
Категория |
| Германия |
Нелегированные стали |
Другие конструкционные стали (не предназначены для термообработки с Rm <500 МПа) |
Химический состав
| Стандарт |
Fe, % |
Si, % |
Mn, % |
P, % |
C, % |
S, % |
|---|
| DIN EN 10346:2015 |
> 97.355 |
< 0.6 |
< 1.7 |
< 0.1 |
< 0.2 |
< 0.045 |
Информация о поставщиках
Properties
| Property |
|---|
| According to EN 10346 Thickness: < 0.35 mm ; yield strength: > 390 MPa |
| According to EN 10346 Thickness: < 0.35 mm ; tensile strength: > 460 MPa |
| According to EN 10346 Thickness: < 0.35 mm ; elongation: > 9 % |
| According to EN 10346 Thickness: 0.35 - 0.50 mm ; yield strength: > 390 MPa |
| According to EN 10346 Thickness: 0.35 - 0.50 mm ; tensile strength: > 460 MPa |
| According to EN 10346 Thickness: 0.35 - 0.50 mm ; elongation: > 12 % |
| According to EN 10346 Thickness: 0.5 - 0.7 mm ; yield strength: > 390 MPa |
| According to EN 10346 Thickness: 0.5 - 0.7 mm ; tensile strength: > 460 MPa |
| According to EN 10346 Thickness: 0.5 - 0.7 mm ; elongation: > 14 % |
| According to EN 10346 Thickness: > 0.7 mm ; yield strength: > 390 MPa |
| According to EN 10346 Thickness: > 0.7 mm ; tensile strength: > 460 MPa |
| According to EN 10346 Thickness: > 0.7 mm ; elongation: > 16 % |
| Density: 7.83 g / cm3 |
Аналоги
| Германия |
Украина |
|---|
| S390GD |
390 |
Стандарты
Описание химических элементов
| Элемент |
Единицы измерений |
Описание |
| Fe |
% |
Железо |
| Si |
% |
Кремний |
| Mn |
% |
Марганец |
| P |
% |
Фосфор |
| C |
% |
Углерод |
| S |
% |
Сера |