1.0039 (S235JRH)
Классификация
| Страна |
Раздел |
Категория |
| Германия |
Нелегированные стали |
Базовые стали |
Химический состав
| Стандарт |
Fe, % |
Mn, % |
P, % |
C, % |
S, % |
N, % |
|---|
| DIN EN 10210-1:2006 |
> 98.311 |
< 1.4 |
< 0.04 |
< 0.2 |
< 0.04 |
< 0.009 |
Информация о поставщиках
Механические свойства при температуре 20 °C
| Прокат |
Стандарт |
Размер, мм |
Напряжение |
Классификаторы |
$$\sigma _{B}$$, $$\textit{МПа}$$ |
$$\sigma_{T}$$, $$\textit{МПа}$$ |
$$\epsilon_L$$, % |
$$KV_{L}$$, $$\textit{Дж}$$ |
Обработка |
|---|
|
|
< 3 |
|
|
360–510 |
|
|
27 |
|
|
|
3–100 |
|
|
360–510 |
|
|
|
|
|
|
100–120 |
|
|
350–500 |
195 |
22 |
|
|
|
|
< 16 |
|
|
|
235 |
|
|
|
|
|
16–40 |
|
|
|
225 |
|
|
|
|
|
40–63 |
|
|
|
215 |
25 |
|
|
|
|
63–80 |
|
|
|
215 |
|
|
|
|
|
80–100 |
|
|
|
215 |
|
|
|
|
|
< 40 |
|
|
|
|
26 |
|
|
|
|
63–100 |
|
|
|
|
24 |
|
|
Properties
| Property |
|---|
| According to EN 10210-1 Thickness: < 3 mm ; yield strength: > 235 MPa |
| According to EN 10210-1 Thickness: < 3 mm ; tensile strength: 360 - 510 MPa |
| According to EN 10210-1 Thickness: 3 - 16 mm ; yield strength: > 235 MPa |
| According to EN 10210-1 Thickness: 3 - 16 mm ; yield strength: 360 - 510 MPa |
| According to EN 10210-1 Thickness: 16 - 40 mm ; yield strength: > 225 MPa |
| According to EN 10210-1 Thickness: 16 - 40 mm ; yield strength: 360 - 510 MPa |
| According to EN 10210-1 Thickness: 40 - 63 mm ; yield strength: > 215 MPa |
| According to EN 10210-1 Thickness: 40 - 63 mm ; yield strength: 360 - 510 MPa |
| According to EN 10210-1 Thickness: 63 - 80 mm ; yield strength: > 215 MPa |
| According to EN 10210-1 Thickness: 63 - 80 mm ; tensile strength: 360 - 510 MPa |
| According to EN 10210-1 Thickness: 80 - 100 mm ; yield strength: > 215 MPa |
| According to EN 10210-1 Thickness: 80 - 100 mm ; yield strength: 360 - 510 MPa |
| According to EN 10210-1 Thickness: 100 - 120 mm ; yield strength: > 195 MPa |
| According to EN 10210-1 Thickness: 100 - 120 mm ; tensile strength: 350 - 500 MPa |
| According to EN 10210-1 Longitudinal samples Thickness: < 40 mm ; elongation: > 26 % |
| According to EN 10210-1 Longitudinal samples Thickness: 40 - 63 mm ; elongation: > 25 % |
| According to EN 10210-1 Longitudinal samples Thickness: 63 - 100 mm ; elongation: > 24 % |
| According to EN 10210-1 Longitudinal samples Thickness: 100 - 120mm ; elongation: > 22 % |
| According to EN 10210-1 Transverse specimens Thickness: < 40 mm ; elongation: > 24 % |
| According to EN 10210-1 Transverse specimens Thickness: 40 - 63 mm ; elongation: > 23 % |
| According to EN 10210-1 Transverse specimens Thickness: 63 - 100 mm ; elongation: > 22 % |
| According to EN 10210-1 Transverse specimens Thickness: 100 - 120mm ; elongation: > 20 % |
| According to EN 10210-1 Test blow Job blow KV at 20°C [68°F]: > 27 j |
| Density: 7.85 g / cm3 |
| Weldability According to ISO / TR 20172 Group: 1.1 |
Аналоги
| Германия |
Украина |
США |
|---|
| S 235 JRH |
Ст3пс-е |
260W |
Стандарты
Описание химических элементов
| Элемент |
Единицы измерений |
Описание |
| Fe |
% |
Железо |
| Mn |
% |
Марганец |
| P |
% |
Фосфор |
| C |
% |
Углерод |
| S |
% |
Сера |
| N |
% |
Азот |
Описание механических свойств
| Параметр |
Единицы измерений |
Описание |
| $$\sigma_{T}$$ |
$$\textit{МПа}$$ |
Предел текучести |
| $$\sigma _{B}$$ |
$$\textit{МПа}$$ |
Предел кратковременной прочности |
| $$\epsilon_L$$ |
% |
Относительное удлинение при растяжении (продольн.) |
| $$KV_{L}$$ |
$$\textit{Дж}$$ |
Работа разрушения при ударе (продольн.) |